AWS EL8 & EM12 & EH14 Low Alloy Submerged ARC Welding Flux

SJ101 is a type of F and alkali based agglomerated flux ,the basicity of which is about 1.8,gary spherical grains is appearance. Is grain size is 2.0-0.28mm(10-60 meshes).SJ101 is suitable for use with AC or DC power, filler wires connect with positive electrode while in DC, the current can reach up to 1200 amps. 

    Sintered submerged arc welding flux SJ101

    Name: Sintered submerged arc welding flux SJ101

    AWS: AWS A5.17/5.23 F6A0-EL8 F7A2-EM12K F7A4-EH14

    SAW wires: EL8, EM12K, EH14, etc.

    Power supply: DC (DCEP), AC

    Basicity: 1.8 BIIW

    Grain size: 10-60 mesh (0.28-2.0mm)

    Alloy transfer: nearly no transfer of Mn, Si to weld metal

    Category: submerged arc welding of mild steel & low-alloy steel

    Industry: structural steel, H beams welding, spiral pipe mills, bridge building, ship building, gas/oil pipeline, heavy equipment, piling pipe, etc.


    Description: fluoride based agglomerated flux. Granular size 10-60 mesh (0.28-2.0mm). Easy slag removal. Excellent mechanical properties. Smooth welding pass. Widely used for API grade X60, X65, X70 pipeline construction. Low diffusible hydrogen content (≤5ml/100g) in weld metal gives it high toughness and high cracking resistance at low temperature. It is appcalible for multi wires welding, especially for double-sided single-pass welding of big diameter vessels. Welding speed is as high as 1.6--1.9m/min.


    Package: damp-proof packing, 25kg/bag

    Certification: ISO


    Chemical Composition of Flux (%)


    SiO₂+TiO₂

    CaO+MgO

    Al₂O₃+MnO

    CaF₂

    S

    P

    20-30

    25-35

    15-30

     15-25

    ≤0.03

    ≤0.08



    Mechanical Properties of Deposit Metal

    Accompanied Wire

    Yield Strength ReH (δs) MPa

    Tensile Strength Rm (σb) MPa

    Elongation A (δ5) %

    Charpy-V lmpact Test (J)

    -20℃-30℃-40℃

    EM12

    ≥420

    500-620

    ≥22

    ≥90

    ≥80

    ≥47

    EH14

    ≥420

    520-680

    ≥22

    ≥90

    ≥80

    ≥47


    Attention:

    1. We get values in data sheets from tests carried out in accordance to AWS and GB standard procedure. They only represent values we get under those conditions. They are not to be taken as guarantees. As to welding, individual test results may vary depending on experience & technique, flux type, base metal, joint preparation, flux preparation, ampere, voltage, etc.

    2. If welding fluxes are stored in improper environment or influenced by condensed moisture, anyway, they get damp, please dry them at 300-350℃ for 2 hours before usage.

    3. Please clean the rust, oil, water on base metal before welding.

    4. Add minumum 20% new flux when using recovered flux to avoid welding defects and maintain welding performance & mechanical properties.

    5. Please control parameters properly, like preheat temperature, interpass temperature, cooling rate.

    DENGFENG, established in 1981, is one of the leading manufacturers and suppliers in China. Should you're interested in our aws el8 & em12 & eh14 low alloy submerged arc welding flux, welcome to buy our quality products with reasonable price. And the wholesale service is also offered in our factory.

Related Products
Inquiry